Minerex will work to Optimize your Business!
Calcined Alumina
Chemical Properties | Unit | AL - 001 | AL - 002 |
---|---|---|---|
Aluminium Oxide (Al₂O₃) | % | 99.6 | 99 |
Silicon Dioxide (SiO₂) | % | 0.03 | 0.04 |
Iron Oxide (Fe₂O₃) | % | 0.03 | 0.03 |
Na₂O total | % | 0.3 | 0.4 |
Na₂O Soluble | % | 0.1 | |
Specific Surface (BET) | m2/g | 1 | 0.70 - 1.50 |
Loss on Ignition [20 - 1100°C] | max 0.30 | ||
𝞪- Al₂O₃ - content | % | 98 | approx. 98 |
Medium grain size diameter | μm | 4 | 4 |
Specific Density | g/cm3 | 3.9 | 3.9 |
Bulk Density | kg/cm3 | 800 | 600 - 800 |
Sinter Temperature | °C | 1750 | 1750 |
Calcined Alumina M100
Chemical Properties | AL - 005 |
---|---|
Al₂O₃ | 99% min |
SiO₂ | 0.035 max |
CaO | 0.08 max |
TiO - ppm | 40 max |
MnO -ppm | 35 max |
Fe₂O₃ | 0.034 max |
Na₂O | 0.53 max |
ZnO- ppm | 150 max |
Moisture(300°C) | |
L.O.l. (300 - 1000°C) | 1.50 max |
Physical analysis | |
Density - (lb/ft2) | |
Superficial Area- (m2/g) | 60.0-90.0 |
Particle Size - (%) | |
+200# | |
+325# | 85 min |
<44μm | 15 max |
>150μm | 15 max |
Calcined Alumina M325
Chemical Properties | AL-006 | AL-007 |
---|---|---|
Al₂O₃ | 98.4 min | 99.1 min |
SiO₂ | 0.074 max | 0.074 max |
Fe₂O₃ | 0.054 max | 0.054 max |
Na₂O-Total | 0.60 max | 0.15 max |
CaO | 0.080 max | |
Moisture (300°C) | 0.5 | 0.50 max |
L.O.l. (300 - 1000°C) | 0.3 | 0.30 max |
Physical Analysis | ||
Density - (g/cm2) | 0.7* | |
Density (Compacted) - (g/cm2) | 1.3* | |
Superficial Area - (m2/g) | Máx 2.2 | 2.0 max |
Glass Primary Size - μm | 2-3* | |
Grain size - (%) | ||
+325# | Máx. 4.0 | 4.0 max |
Particle Size Distribution - μm | ||
D90 | 27* | 6.-26 |
D50 | 4* | 2.-7 |
D10 | 2* |
Calcium Carbonate
Properties | CH - 003 - HF15 | CH - 003 - HF03 | CH - 003 - HF1R |
---|---|---|---|
Particle Size (D50%) | 12.90 (μm) | 4.40 (μm) | 1.96 μm |
%+325 Mesh Residue (ISO 787/7) | 0.46% | 1833.00% | 1536.00% |
Particle< 2 μm (Sedigraph) | 6.40% | 31.70% | 50.60% |
Specific Area BET (ASTM 958-92) | 0.80 m2/gr | 3.60 m2/gr | 4.80 m2/gr. |
Whiteness (Minolta CIE) | 96.1 | 96.4 | 95.5 |
Oil Absorbtion (ISO 787/5) | 22.00 gr / 100.00gr | 25.00 gr / 100.00gr | 27.00 gr/ 100.00gr |
Moisture (ISO 787/2) | 0.00% | 0.07% | 0.001 |
Specific Weight | 2.70 gr/cm3 | 2.70 gr/cm3 | 2.70 gr/cm3 |
Bulk Density (ASTM C-29) | 1.00 - 1.30 gr/cm3 | 0.70 - 0.90 gr/cm3 | 0.60 - 0.80 gr/cm3 |
Caracteristicas Fisicas | HI FILL 15 | HI FILL 3 | HI FILL 1R |
---|---|---|---|
Tamaño medio de partícula (D50%) | 12.90 (μm) | 4.40 (μm) | 1.96 μm |
% retenido en malla 325 (ISO 787/7) | 0.46% | 1833.00% | 1536.00% |
Partículas < 2 μm (Sedigraph) | 6.40% | 31.70% | 50.60% |
Superficie específica BET (ASTM 958-92) | 0.80 m2/gr | 3.60 m2/gr | 4.80 m2/gr. |
Blancura (Minolta CIE) | 96.10 | 96.40 | 95.50 |
Absorción de Aceite (ISO 787/5) | 22.00 gr / 100.00gr | 25.00 gr / 100.00gr | 27.00 gr/ 100.00gr |
Humedad (ISO 787/2) | 0.00% | 0.07% | 0.001 |
Peso específico | 2.70 gr/cm3 | 2.70 gr/cm3 | 2.70 gr/cm3 |
Densidad de bulto (ASTM C-29) | 1.00 - 1.30 gr/cm3 | 0.70 - 0.90 gr/cm3 | 0.60 - 0.80 gr/cm3 |
Fly Ash
Chemical Properties | Unit | CH-005-A | CH - 005-B | CH - 005-C |
---|---|---|---|---|
SiO₂ + Al₂O₃ + Fe₂O₃ | min % | 70 | 50 | 70 |
SO₃ | max % | 5 | 5 | 4 |
Moisture Content | max % | 3 | 3 | 3 |
Loss on Ignition | max % | 6 | 6 | 10 |
Optional Chemical | ||||
Available Alkalies | max % | 1.5 | 1.5 | 1.5 |
Physical | ||||
Fineness + 325 Mesh | max % | 34 | 34 | 34 |
Strength Activity/Cem. | min % | 75 | 75 | 75 |
Water Requirement | max % | 105 | 105 | 105 |
Autoclave Expansion | max % | 0.8 | 0.8 | 0.8 |
Uniformity Requirements | ||||
Density Max. Var. | max % | 5 | 5 | 5 |
Fineness Points Var. | max % | 5 | 5 | 5 |
Optional Physical | ||||
Multiple Factor | 225 | - | - | |
Increase In Drying Shrinkage | max % | 0.03 | 0.03 | 0.03 |
Uniformity Requirements | ||||
A.E. Admixture Demand | max % | 20 | 20 | 20 |
Control of ASR | ||||
Expansion, % of Low Alkali Cement | max % | 100 | 100 | 100 |
Sulfate Resistance | ||||
Moderate Exposure, 6 months | max % | 0.1 | 0.1 | 0.1 |
High Exposure, 6 months | max % | 0.05 | 0.05 | 0.05 |
Propiedades Químicas | Fly ash F | Fly ash C | Fly ash N | |
---|---|---|---|---|
SiO₂ + Al₂O₃ + Fe₂O₃ | min % | 70.00 | 50.00 | 70.00 |
SO₃ | max % | 5.00 | 5.00 | 4.00 |
Contenido de Húmedad | max % | 3.00 | 3.00 | 3.00 |
Perdida en Ignición | max % | 6.00 | 6.00 | 10.00 |
Opcionales | ||||
Alcalinos Disponibles | max % | 1.50 | 1.50 | 1.50 |
Propiedades Físicas | ||||
Finura + malla 325 | max % | 34.00 | 34.00 | 34.00 |
Actividad de fuerza | min % | 75.00 | 75.00 | 75.00 |
Requisitos de agua | max % | 105.00 | 105.00 | 105.00 |
Expansion autoclave | max % | 0.80 | 0.80 | 0.80 |
Requisitos de uniformidad | ||||
Densidad Max. Var. | max % | 5.00 | 5.00 | 5.00 |
Puntos de finura Var. | max % | 5.00 | 5.00 | 5.00 |
Opcionales | ||||
Factor Míltiple | 225.00 | - | - | |
Aumento de la contracción por secado | max % | 0.03 | 0.03 | 0.03 |
Requisitos de Uniformidad | ||||
Demanda de mezcla A.E. | max % | 20.00 | 20.00 | 20.00 |
Control de ASR | ||||
Expansion, % de cemento de bajo contenido alcalino | max % | 100.00 | 100.00 | 100.00 |
Resistencia al sulfato | ||||
Exposición Moderada, 6 months | max % | 0.10 | 0.10 | 0.10 |
Exposición Alta, 6 months | max % | 0.05 | 0.05 | 0.05 |
Barium Carbonate
Chemical Properties | BA-001 |
---|---|
Appearance | Powder & Granule |
BaCO₃ | 99.2% min |
SO4 | 0.35% max |
Fe | 0.004% max |
HCI Insoluble | .25% max |
Moisture | 0.3% max |
Bulk. Density. Heavy Type Light Type |
1.48 g/cm3 min 1.21g/cm3 max |
Sodium Hexamethaphosphate
SO - 001 | ||
---|---|---|
Chemical Properties | Lower Limit | Upper Limit |
Appearance | white | powder |
Total phosphate P₂O5 | 68% | |
Inactive phosphate as P₂O5 | 7.50% | |
Water insoluble | 200 ppm | |
Iron as Fe | 150 ppm | |
pH VALUE (1% SOLUTION) | 5.8 | 7.3 |
Through 60 mesh | 90% |
Titanium Dioxide
Chemical Properties | TI - 003 (Enamel Grade) |
---|---|
TiO₂ | 98.5% min |
S | 0.06% max |
Fe₂O₃ | 0.05% max |
P | 1% max |
Residue on 320 mesh sieve (45 μm) | 0.5% max |
Particle Size | D50 1.5 μm - 2.0 μm, D90 6-10 μm |
Chemical Properties | TI-004 (Anatase Grade) |
---|---|
TiO₂ | 98.5% min |
Dry Powder Whiteness | 95.0 min |
Tint-reducing Power (Compared with the standard sample) | 105 min |
Oil Absorption (g/100) | 26 max |
105 °C Volatile (%) | 0.5 max |
45 μm Residue (%) | 0.3 max |
PH of water suspension | 6.5 - 8.5 |
Matter soluble in water | 0.5 |
Zirconium Silicate
Chemical Properties | ZI -003 |
---|---|
Zr(Hf)O₂ | ≥64 |
Fe₂O₃ | ≤0.1 |
TiO₂ | ≤0.2 |
Particle Side | D50 0.8-1.0 um |
Whitemess % (1200 C°*10 min) | ≥95 |
Ig. Loss(1025 °C - 2h, H₂O Containing) % | ≤0.8 |
Zircon Powder (M200)
Chemical Properties | ZI - 007 |
---|---|
ZrO₂ | ≥65 |
Fe₂O₃ | ≤0.15 |
TiO₂ | ≤0.15 |
Particle Size 200 mesh | 95% pass 200 mesh |
Whitemess % (1200 C°*10 min) | ≥70 |
Ig. Loss (1025 °C - 2h, H₂O Containing) % | ≤0.2 |